DRIVING FORWARD

HarbisonWalker International (HWI) manufactures a variety of mortars for a wide range of applications, service conditions, and purposes.

All major chemistry types are represented, as well as bond types and shipping condition options. HWI's mortars have been developed to meet specific service conditions and to serve several purposes. These functions include bonding the brickwork for structural strength to reduce chemical attack from corrosive slags or gases, and to match the properties of the brick with which they are used.

Purpose of Mortar >

Fill joints, bond individual bricks together, and even out irregularities of brick face
Correct for imperfections in steel shell when laying up brick
Protect joints from attack by slag or other fluxes
To limit the passage of gases through the refractory structure
Provide a protective coating for patching and brushing
Not intended to strengthen lining in most applications

Choosing a Mortar >

Match or exceed brick chemistry/quality
Account for service conditions
Bond type consideration
Desired consistency (depends on application)
Wet vs. Dry packaging

Bond Technology
Selecting a bond type is a critical decision when choosing a mortar. HarbisonWalker
International’s products offer three bonding options >

AIR-SET BOND

Takes a rigid set when dried over 110°C. Air-setting mortars help maintain the strength of the bond up to the temperature at which the ceramic bond takes effect.

Sodium silicate
Forms a strong bond when heated above 100°C

Consideration:
Water soluble until over 343°C

HEAT-SET BOND

Develops a ceramic set with a strong bond only at high furnace temperatures. These mortars offer expansion flexibility during initial heating.

Forms a ceramic bond at high temperatures. No bond is formed until the product reaches above 1315°C to fuse particles
Allows brick to expand at high temperatures before the mortar gains max strength

PHOSPHATE BOND
Often grouped with heat-setting mortars, but these mortars see a chemical reaction occur at lower temperatures (260°- 316°C) between the phosphoric acid and ceramic oxides. This reaction imparts high strength to the mortar joint and usually offers the best resistance to severe slag attack.

Will develop a strong chemical bond above 343°C
Some expansion will be taken up by the mortar joint, but nothing after chemical bond is formed.

Considerations:
Phosphate can be detrimental to the process
Water soluble until over 343°C

04.05.2021, HarbisonWalker International

Notícias sobre o material do site é copyright e pertence à empresa ou ao seu fornecedor de terceiros notícia, e todos os direitos reservados. Qualquer usuário que acessa esse material poderá fazê-lo apenas para seu próprio uso pessoal, bem como a utilização desse material é de risco exclusivo do Utilizador. A redistribuição ou exploração comercial de material tal notícia é expressamente proibida. Se tal notícia material é fornecido por um terceiro, cada utilizador concorda em observar e estar vinculado aos termos específicos de utilização aplicáveis a material notícia. Nós não representamos nem endossamos a precisão ou confiabilidade de qualquer informação contida em qualquer notícia ou sites externos referidos na notícia.

Should the content or the design of these sites violate third parties rights or legal prescriptions, we kindly ask you to send us a respective message without invoice or cost. We guarantee that passages where the claim is considered as justified will be removed immediately, without any necessity to involve any lawyer into this issue. We will reject any claim caused by submission of a honorary note in this regard without any prior contact and confirmation of the issueby us and we reserve the right ssue counter claim ourselves because of violation of aforesaid conditions.